Overview
ASTM A335 P9 is a specialized seamless ferritic alloy steel pipe for high-temperature service. It is commonly used in power plants and petrochemical industries for applications requiring high-temperature resistance and toughness. The chemical composition includes chromium, molybdenum, and vanadium, which provide excellent corrosion resistance, high strength, and good weldability. ASTM A335 P9 has a maximum working temperature of 600°C and a maximum operating pressure of 65 bar.
Molybdenum Feature
The A335 pipes has a high level of Chromium and Molybdenum presence in it. While Molybdenum increases the overall strength, resistance, elasticity, hardenability and overall quality, moly ensures that the material is more resistant to softening, restrains the growth of grains and lessens the chances of embrittlement. It is the single additive that is responsible for the increase in high temperature resistance and it also improves the corrosion resistance to steel
ASTM A335 Feature
High-temperature resistance: ASTM A335 seamless steel pipe is designed to withstand high temperatures up to 600°C (1112°F), making it an ideal material for high-temperature applications such as steam pipelines and heat exchangers.
Corrosion resistance: ASTM A335 seamless steel pipe exhibits good corrosion resistance in aggressive environments, such as those found in chemical processing and oil and gas industries.
High strength: ASTM A335 seamless steel pipe has high tensile strength and yield strength, making it ideal for use in high-pressure applications. Good weldability: ASTM A335 seamless steel pipe can be easily welded using traditional methods, with no need for preheating or post-weld heat treatment.
Uniform properties: ASTM A335 seamless steel pipe is produced using a consistent manufacturing process, ensuring that each pipe has uniform properties and quality.
Cost-effective: Despite its superior properties, ASTM A335 seamless steel pipe remains an affordable option for high-temperature applications.
Chemical Composition
| Grade | UNS | C≤ | Mn | P≤ | S≤ | Si≤ | Cr | Mo |
| P9 | S50400 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 8-10.00 | 0.44-0.65 |
Mechanical Properties
| Mechanical properties | Tensile, min, ksi[MPa] | Yield,min, ksi[MPa] | Elongation, %(min) | Hardness, HB(max) |
| P9 | 60[415] | 30[205] | 30 | - |
Elongation
Elongation in 2 in or 50mm or 4D minimum%:
For wall thickness 5/16 in [8mm] and over: Longitudinal 30% and Transverse 20%.
Elongation smaller 2 in or 50mm or 4D minimum%:
For wall thickness 5/16 in [8mm] and over: Longitudinal 22% and Transverse 14%.
For strip tests a deduction of each 0.8mm below 8mm shall be calculated with the Table 5 in ASTM A335.
Test
Tensile tests: Transverse and Longitudinal
Flattening test of ASTM A999/A999M
Hardness test not exceeding 250 HBW/265 HV30 [25HRC]
Bend Test shall be carried as per ASTM A370
Hydrostatic Test is required, depending on the buyer’s decision both Hydrostatic test and a nondestructive test could be carried out.
Use
power plants and chemical plants
construction of industrial furnaces
aerospace industry
medical field
food processing industry
coins and medals
electrical components
Advantage
1.Withstand high temperatures and has good corrosion resistance.
2. biocompatible and can be used in implants and other medical devices.
3.non-toxic
Package Process
1.with plastic cap to protect both ends
2.weaving bag wrapped outside the pipe
3.then pack into wooden case.